Ti(IV) was grafted onto the frameworks of MCM-41 material by solution grafting reaction scheme. The product was extensively characterized by XRD, TEM, EDS, and N₂ adsorption-desorption isotherms as well as FTIR and ²⁹Si MAS NMR methods. Three mechanisms of the solution grafting reaction were put forward. Experimental results show that the Si-OH groups react with Ti(OBu)₄ and form Si-O-Ti bands, which are marked by the strong absorption at 950-960 cm^-1 in IR spectra.

源语言	英语
页（从-至）	87-92
页数	6
期刊	Wuji Cailiao Xuebao/Journal of Inorganic Materials
卷	16
期	1
出版状态	已出版 - 1月 2001
已对外发布	是

其它文件与链接

链接到 Scopus 的出版物

引用此

@article{d59947fe6f07421baec3202cd6a4b851,

title = "Solution grafting of Ti(IV) inside MCM-41 materials",

abstract = "Ti(IV) was grafted onto the frameworks of MCM-41 material by solution grafting reaction scheme. The product was extensively characterized by XRD, TEM, EDS, and N2 adsorption-desorption isotherms as well as FTIR and 29Si MAS NMR methods. Three mechanisms of the solution grafting reaction were put forward. Experimental results show that the Si-OH groups react with Ti(OBu)4 and form Si-O-Ti bands, which are marked by the strong absorption at 950-960 cm-1 in IR spectra.",

keywords = "Mesoporous materials, Solution grafting",

author = "Zhang, \{W. H.\} and Shi, \{J. L.\} and Chen, \{H. R.\} and Yan, \{J. N.\} and Hua, \{Z. L.\} and Yan, \{D. S.\}",

year = "2001",

month = jan,

language = "英语",

volume = "16",

pages = "87--92",

journal = "Wuji Cailiao Xuebao/Journal of Inorganic Materials",

issn = "1000-324X",

publisher = "Science Press ",

number = "1",

}

TY - JOUR

T1 - Solution grafting of Ti(IV) inside MCM-41 materials

AU - Zhang, W. H.

AU - Shi, J. L.

AU - Chen, H. R.

AU - Yan, J. N.

AU - Hua, Z. L.

AU - Yan, D. S.

PY - 2001/1

Y1 - 2001/1

N2 - Ti(IV) was grafted onto the frameworks of MCM-41 material by solution grafting reaction scheme. The product was extensively characterized by XRD, TEM, EDS, and N2 adsorption-desorption isotherms as well as FTIR and 29Si MAS NMR methods. Three mechanisms of the solution grafting reaction were put forward. Experimental results show that the Si-OH groups react with Ti(OBu)4 and form Si-O-Ti bands, which are marked by the strong absorption at 950-960 cm-1 in IR spectra.

AB - Ti(IV) was grafted onto the frameworks of MCM-41 material by solution grafting reaction scheme. The product was extensively characterized by XRD, TEM, EDS, and N2 adsorption-desorption isotherms as well as FTIR and 29Si MAS NMR methods. Three mechanisms of the solution grafting reaction were put forward. Experimental results show that the Si-OH groups react with Ti(OBu)4 and form Si-O-Ti bands, which are marked by the strong absorption at 950-960 cm-1 in IR spectra.

KW - Mesoporous materials

KW - Solution grafting

UR - https://www.scopus.com/pages/publications/0034864458

M3 - 文章

AN - SCOPUS:0034864458

SN - 1000-324X

VL - 16

SP - 87

EP - 92

JO - Wuji Cailiao Xuebao/Journal of Inorganic Materials

JF - Wuji Cailiao Xuebao/Journal of Inorganic Materials

IS - 1

ER -

Solution grafting of Ti(IV) inside MCM-41 materials

摘要

其它文件与链接

指纹

引用此