TY - GEN
T1 - Resistivity and dielectric properties of Bi1/2Na 1/2TiO3-mixed (Ba,Sr)TiO3 ceramics
AU - Hoshi, Y.
AU - Xiang, P. H.
AU - Takeda, H.
AU - Nishida, T.
AU - Uchiyama, K.
AU - Shiosaki, T.
PY - 2007
Y1 - 2007
N2 - In order to prepare lead-free BaTi03-based positive temperature coefficient of resistance (abbreviated to PTCR) ceramics, 2.0, 4.0, 6.0, 8.0, 10 mol% of Bi1/2Na1/2TiO3 (abbreviated to BNT) added Ba0.92Sr0.08TiO3 (abbreviated to BST) were fabricated by the conventional solid state reaction. Phase and microstructure characterizations revealed that no obvious BNT phase was found in the final sintered BNT-added BST ceramics, indicating that the BNT phase and BST phase formed a solid-solution during sintering. Without doping other special elements, an obvious PTCR effect was observed in the BNT-added BST samples sintered at 1350 °C in air. To reveal the origin of PTCR effect in the BNT-added BST ceramics, the dielectric properties were also investigated. The BNT-mixed BST (abbreviated to BST-BNT) PTCR ceramics exhibited higher Curie temperatures than that of BST sample.
AB - In order to prepare lead-free BaTi03-based positive temperature coefficient of resistance (abbreviated to PTCR) ceramics, 2.0, 4.0, 6.0, 8.0, 10 mol% of Bi1/2Na1/2TiO3 (abbreviated to BNT) added Ba0.92Sr0.08TiO3 (abbreviated to BST) were fabricated by the conventional solid state reaction. Phase and microstructure characterizations revealed that no obvious BNT phase was found in the final sintered BNT-added BST ceramics, indicating that the BNT phase and BST phase formed a solid-solution during sintering. Without doping other special elements, an obvious PTCR effect was observed in the BNT-added BST samples sintered at 1350 °C in air. To reveal the origin of PTCR effect in the BNT-added BST ceramics, the dielectric properties were also investigated. The BNT-mixed BST (abbreviated to BST-BNT) PTCR ceramics exhibited higher Curie temperatures than that of BST sample.
UR - https://www.scopus.com/pages/publications/51349139590
U2 - 10.1109/ISAF.2007.4393414
DO - 10.1109/ISAF.2007.4393414
M3 - 会议稿件
AN - SCOPUS:51349139590
SN - 1424413338
SN - 9781424413331
T3 - IEEE International Symposium on Applications of Ferroelectrics
SP - 823
EP - 824
BT - 2007 16th IEEE International Symposium on the Applications of Ferroelectrics, ISAF
T2 - 2007 16th IEEE International Symposium on the Applications of Ferroelectrics, ISAF
Y2 - 27 May 2007 through 31 May 2007
ER -