Mesostructured amorphous manganese oxides: Facile synthesis and highly durable elimination of low-concentration NO at room temperature in air

Yanyan Du; Zile Hua; Weimin Huang; Meiying Wu; Min Wang; Jin Wang; Xiangzhi Cui; Lingxia Zhang; Hangrong Chen; Jianlin Shi

doi:10.1039/c5cc00269a

Mesostructured amorphous manganese oxides: Facile synthesis and highly durable elimination of low-concentration NO at room temperature in air

Yanyan Du
, Zile Hua
, Weimin Huang
, Meiying Wu
, Min Wang
, Jin Wang
, Xiangzhi Cui
, Lingxia Zhang
, Hangrong Chen
, Jianlin Shi^*

^*此作品的通讯作者

CAS - Shanghai Institute of Ceramics

科研成果: 期刊稿件 › 文章 › 同行评审

32 引用（Scopus）

摘要

At a high space velocity of 120000 mL g^-1 h^-1 and a relative humidity of 50-90%, 98% removal of 10 ppm NO has been achieved for over 237 h and no sign of deactivation was observed with mesostructured amorphous manganese oxides (AMO), due to the prevention of the catalyst active sites from deactivation.

源语言	英语
页（从-至）	5887-5889
页数	3
期刊	Chemical Communications
卷	51
期	27
DOI	https://doi.org/10.1039/c5cc00269a
出版状态	已出版 - 7 4月 2015
已对外发布	是

访问文件

10.1039/c5cc00269a

其它文件与链接

链接到 Scopus 的出版物

引用此

@article{155e7331379e4da994690d0951300f5e,

title = "Mesostructured amorphous manganese oxides: Facile synthesis and highly durable elimination of low-concentration NO at room temperature in air",

abstract = "At a high space velocity of 120000 mL g-1 h-1 and a relative humidity of 50-90\%, 98\% removal of 10 ppm NO has been achieved for over 237 h and no sign of deactivation was observed with mesostructured amorphous manganese oxides (AMO), due to the prevention of the catalyst active sites from deactivation.",

author = "Yanyan Du and Zile Hua and Weimin Huang and Meiying Wu and Min Wang and Jin Wang and Xiangzhi Cui and Lingxia Zhang and Hangrong Chen and Jianlin Shi",

note = "Publisher Copyright: {\textcopyright} The Royal Society of Chemistry 2015.",

year = "2015",

month = apr,

day = "7",

doi = "10.1039/c5cc00269a",

language = "英语",

volume = "51",

pages = "5887--5889",

journal = "Chemical Communications",

issn = "1359-7345",

publisher = "Royal Society of Chemistry",

number = "27",

}

TY - JOUR

T1 - Mesostructured amorphous manganese oxides

T2 - Facile synthesis and highly durable elimination of low-concentration NO at room temperature in air

AU - Du, Yanyan

AU - Hua, Zile

AU - Huang, Weimin

AU - Wu, Meiying

AU - Wang, Min

AU - Wang, Jin

AU - Cui, Xiangzhi

AU - Zhang, Lingxia

AU - Chen, Hangrong

AU - Shi, Jianlin

PY - 2015/4/7

Y1 - 2015/4/7

N2 - At a high space velocity of 120000 mL g-1 h-1 and a relative humidity of 50-90%, 98% removal of 10 ppm NO has been achieved for over 237 h and no sign of deactivation was observed with mesostructured amorphous manganese oxides (AMO), due to the prevention of the catalyst active sites from deactivation.

AB - At a high space velocity of 120000 mL g-1 h-1 and a relative humidity of 50-90%, 98% removal of 10 ppm NO has been achieved for over 237 h and no sign of deactivation was observed with mesostructured amorphous manganese oxides (AMO), due to the prevention of the catalyst active sites from deactivation.

UR - https://www.scopus.com/pages/publications/84925374884

U2 - 10.1039/c5cc00269a

DO - 10.1039/c5cc00269a

M3 - 文章

AN - SCOPUS:84925374884

SN - 1359-7345

VL - 51

SP - 5887

EP - 5889

JO - Chemical Communications

JF - Chemical Communications

IS - 27

ER -

Mesostructured amorphous manganese oxides: Facile synthesis and highly durable elimination of low-concentration NO at room temperature in air

摘要

访问文件

其它文件与链接

指纹

引用此