Effect of B₂O₃ on the sintering and microwave dielectric properties of M-phase LiNb_0.6Ti_0.5O₃ ceramics

The effect of B₂O₃ addition on the sintering, microstructure and the microwave dielectric properties of LiNb_0.6Ti_0.5O₃ ceramics have been investigated. It is found that low-level doping of B₂O₃ (≤2 wt.%) can significantly improve the densification and dielectric properties of LiNb_0.6Ti_0.5O₃ ceramics. Due to the liquid phase effect of B₂O₃ addition, LiNb_0.6Ti_0.5O₃ ceramics could be sintered to a theoretical density higher than 95% even at 880 °C. No secondary phase was observed for the B₂O₃-doped ceramics. There is no obvious degradation in dielectric properties for the ceramics with B₂O₃ additions. In the case of 1 wt.% B₂O₃ addition, the ceramics sintered at 880 °C show good microwave dielectric properties of ε_r = 70, Q × f = 5400 GHz, τ_f = -6.39 ppm/°C. It represents that the ceramics could be promising for multilayer low-temperature co-fired ceramics (LTCC) applications.