A comparative study of field emission properties of carbon nanotube films prepared by vacuum filtration and screen-printing

Min Qian; Tao Feng; Kai Wang; Hui Ding; Yiwei Chen; Zhuo Sun

doi:10.1016/j.apsusc.2010.02.064

A comparative study of field emission properties of carbon nanotube films prepared by vacuum filtration and screen-printing

Min Qian
, Tao Feng^*
, Kai Wang
, Hui Ding
, Yiwei Chen
, Zhuo Sun

^*此作品的通讯作者

Ministry of Education of the People's Republic of China

科研成果: 期刊稿件 › 文章 › 同行评审

22 引用（Scopus）

摘要

A comprehensive comparative study of electron field emission properties of carbon nanotube (CNT) films prepared by vacuum filtration and screen-printing was carried out. Field emission performance of vacuum filtered CNT films with different filtered CNT suspension volumes was systematically studied, and the optimum electron emission was obtained with a low turn on field of ∼0.93 V/μm (at 1 μA/cm ² ) and a high field enhancement factor β of ∼9720. Comparing with screen-printed CNT films, vacuum filtered CNT films showed better electron emission performance, longer lifetime, and greater adhesive strength to substrates. This work reveals a potential use of vacuum filtered CNT films as field emission cathodes.

源语言	英语
页（从-至）	4642-4646
页数	5
期刊	Applied Surface Science
卷	256
期	14
DOI	https://doi.org/10.1016/j.apsusc.2010.02.064
出版状态	已出版 - 1 5月 2010
已对外发布	是

访问文件

10.1016/j.apsusc.2010.02.064

其它文件与链接

链接到 Scopus 的出版物

引用此

@article{2bfb715f1c7940158c35474c77377c41,

title = "A comparative study of field emission properties of carbon nanotube films prepared by vacuum filtration and screen-printing",

abstract = " A comprehensive comparative study of electron field emission properties of carbon nanotube (CNT) films prepared by vacuum filtration and screen-printing was carried out. Field emission performance of vacuum filtered CNT films with different filtered CNT suspension volumes was systematically studied, and the optimum electron emission was obtained with a low turn on field of ∼0.93 V/μm (at 1 μA/cm 2 ) and a high field enhancement factor β of ∼9720. Comparing with screen-printed CNT films, vacuum filtered CNT films showed better electron emission performance, longer lifetime, and greater adhesive strength to substrates. This work reveals a potential use of vacuum filtered CNT films as field emission cathodes.",

keywords = "Carbon nanotube, Field emission, Screen-printing, Vacuum filtration",

author = "Min Qian and Tao Feng and Kai Wang and Hui Ding and Yiwei Chen and Zhuo Sun",

year = "2010",

month = may,

day = "1",

doi = "10.1016/j.apsusc.2010.02.064",

language = "英语",

volume = "256",

pages = "4642--4646",

journal = "Applied Surface Science",

issn = "0169-4332",

publisher = "Elsevier B.V.",

number = "14",

}

TY - JOUR

T1 - A comparative study of field emission properties of carbon nanotube films prepared by vacuum filtration and screen-printing

AU - Qian, Min

AU - Feng, Tao

AU - Wang, Kai

AU - Ding, Hui

AU - Chen, Yiwei

AU - Sun, Zhuo

PY - 2010/5/1

Y1 - 2010/5/1

N2 - A comprehensive comparative study of electron field emission properties of carbon nanotube (CNT) films prepared by vacuum filtration and screen-printing was carried out. Field emission performance of vacuum filtered CNT films with different filtered CNT suspension volumes was systematically studied, and the optimum electron emission was obtained with a low turn on field of ∼0.93 V/μm (at 1 μA/cm 2 ) and a high field enhancement factor β of ∼9720. Comparing with screen-printed CNT films, vacuum filtered CNT films showed better electron emission performance, longer lifetime, and greater adhesive strength to substrates. This work reveals a potential use of vacuum filtered CNT films as field emission cathodes.

AB - A comprehensive comparative study of electron field emission properties of carbon nanotube (CNT) films prepared by vacuum filtration and screen-printing was carried out. Field emission performance of vacuum filtered CNT films with different filtered CNT suspension volumes was systematically studied, and the optimum electron emission was obtained with a low turn on field of ∼0.93 V/μm (at 1 μA/cm 2 ) and a high field enhancement factor β of ∼9720. Comparing with screen-printed CNT films, vacuum filtered CNT films showed better electron emission performance, longer lifetime, and greater adhesive strength to substrates. This work reveals a potential use of vacuum filtered CNT films as field emission cathodes.

KW - Carbon nanotube

KW - Field emission

KW - Screen-printing

KW - Vacuum filtration

UR - https://www.scopus.com/pages/publications/77950596076

U2 - 10.1016/j.apsusc.2010.02.064

DO - 10.1016/j.apsusc.2010.02.064

M3 - 文章

AN - SCOPUS:77950596076

SN - 0169-4332

VL - 256

SP - 4642

EP - 4646

JO - Applied Surface Science

JF - Applied Surface Science

IS - 14

ER -

A comparative study of field emission properties of carbon nanotube films prepared by vacuum filtration and screen-printing

摘要

访问文件

其它文件与链接

学术指纹

引用此